| Industry | Applications |
|---|---|
| Aerospace | Lightweight structural parts, aircraft components |
| Automotive | Automotive brackets, lightweight chassis components |
| Mold & Tooling | Customized molds and tooling parts |
| Industrial Equipment | High-strength mechanical components |
| Lightweight Design | Topology-optimized and complex structures |
| Element | Content |
|---|---|
| Aluminum (Al) | Balance |
| Magnesium (Mg) | ≤1.20% |
| Silicon (Si) | ≤0.80% |
| Iron (Fe) | ≤0.70% |
| Manganese (Mn) | ≤0.15% |
| Titanium (Ti) | ≤0.15% |
| Zinc (Zn) | ≤0.25% |
| Copper (Cu) | ≤0.40% |
| Chromium (Cr) | ≤0.35% |
| Property | Specification |
|---|---|
| Powder Particle Size | 15–53 μm |
| D10 | ≥15 μm |
| D50 | 30–40 μm |
| D90 | ≤62 μm |
| Oxygen Content | ≤0.10% |
| Apparent Density | ≥1.0 g/cm³ |
| Tap Density | ≥1.3 g/cm³ |
| Flowability | ≤110 s / 50 g |
| Powder Sphericity | ≥90% |
| Property | Value |
|---|---|
| Tensile Strength | ≥290 MPa |
| Yield Strength | ≥250 MPa |
| Elongation | ≥15% |
| Treatment | Condition |
|---|---|
| Aging Treatment | 375°C × 6h / Air Cooling |
| Feature | Description |
|---|---|
| Lightweight | Excellent strength-to-weight ratio |
| High Strength | Suitable for structural applications |
| Good Ductility | High elongation and toughness |
| Corrosion Resistance | Suitable for aerospace and automotive environments |
| Excellent Printability | Stable powder flow and good forming performance |
| Complex Geometry Capability | Ideal for topology optimization and lightweight designs |